Maintenance
Coatings for all industrial environments. Maintenance products
for repairing & rebuilding plant equipment |
 |
| |
An elastomeric epoxy urethane caulk which combines
the flexibility of a urethane with the chemical resistance
and adhesion of an epoxy. |
|
Density
(g/ml) |
Coverage
(in 3/kg) |
Mix Ratio by
Weight 1 |
Mix Ratio by
Volume 1 |
Max/Min Build/Coat
(mils) |
| 1.19 |
52 |
3:1 |
3:1 |
500/30 |
Number of
Coats |
Working Time
(minutes) |
Minimum Application
Temp (F/C) |
Max Dry Operating
Temp (F/C) |
Dry to Touch
(hours) |
| 1 |
60 |
40/4 |
250/122 |
8 |
Recoat Time
(min/max hours) |
Functional Cure 2
(hours) |
Full Cure
(hours) |
Surface Preparation
Methods 3 |
pH Range
5 |
| 6/24 |
36 |
120 |
SSPC-3,11 |
2.0-14 |
A fast curing brushable coating material with outstanding
chemical resistance. It can be used to make quick repairs
on existing linings or for small coating or patching
projects. It is supplied in an easy to use pouch for
convenient mixing. |
|
Density
(g/ml) |
Coverage
(in 3/kg) |
Mix Ratio by
Weight 1 |
Mix Ratio by
Volume 1 |
Max/Min Build/Coat
(mils) |
| 1.1 |
3in3/50gr |
n/a |
n/a |
40/10 |
Number of
Coats |
Working Time
(minutes) |
Minimum Application
Temp (F/C) |
Max Dry Operating
Temp (F/C) |
Dry to Touch
(hours) |
| 1 |
15 |
65/18 |
375/190 |
1 |
Recoat Time
(min/max hours) |
Functional Cure 2
(hours) |
Full Cure
(hours) |
Surface Preparation
Methods 3 |
pH Range
5 |
| 1/3 |
6 |
24 |
SSPC-3,11 |
0.5-14 |
An extremely fast curing putty material, packaged
in a single tube for easy mixing and use. Ideal for
storing in toolboxes to make quick repairs or to stop
leaks in steel, aluminum, fiberglass or concrete. |
|
Density
(g/ml) |
Coverage
(in 3/kg) |
Mix Ratio by
Weight 1 |
Mix Ratio by
Volume 1 |
Max/Min Build/Coat
(mils) |
| 1.9 |
30 |
n/a |
n/a |
500/30 |
Number of
Coats |
Working Time
(minutes) |
Minimum Application
Temp (F/C) |
Max Dry Operating
Temp (F/C) |
Dry to Touch
(hours) |
| 1 |
2 |
32/0 |
300/150 |
20
minutes |
Recoat Time
(min/max hours) |
Functional Cure 2
(hours) |
Full Cure
(hours) |
Surface Preparation
Methods 3 |
pH Range
5 |
| 20
minutes |
20
minutes |
1 |
SSPC-3,11 |
1.5-14 |
A brushable, fast curing, high temperature polyurethane
with excellent abrasion resistance. It is used primarily
for conveyer belt repair or as a gasket material. Shore
A is 80. |
|
Density
(g/ml) |
Coverage
(in 3/kg) |
Mix Ratio by
Weight 1 |
Mix Ratio by
Volume 1 |
Max/Min Build/Coat
(mils) |
| 0.93 |
57 |
1.2:1 |
3:2 |
40/10 |
Number of
Coats |
Working Time
(minutes) |
Minimum Application
Temp (F/C) |
Max Dry Operating
Temp (F/C) |
Dry to Touch
(hours) |
| 1-2 |
30 |
65/18 |
200/94 |
2 |
Recoat Time
(min/max hours) |
Functional Cure 2
(hours) |
Full Cure
(hours) |
Surface Preparation
Methods 3 |
pH Range
5 |
| 2/24 |
24 |
72 |
SSPC-3,11 |
3.0-10 |
An underwater version of the EAC used for resurfacing
or painting underwater vessels, pilings or other similar
items. |
|
Density
(g/ml) |
Coverage
(in 3/kg) |
Mix Ratio by
Weight 1 |
Mix Ratio by
Volume 1 |
Max/Min Build/Coat
(mils) |
| 1.6 |
36 |
3.8:1 |
2:1 |
30/10 |
Number of
Coats |
Working Time
(minutes) |
Minimum Application
Temp (F/C) |
Max Dry Operating
Temp (F/C) |
Dry to Touch
(hours) |
| 2-3 |
40 |
50/10 |
250/122 |
12 |
Recoat Time
(min/max hours) |
Functional Cure 2
(hours) |
Full Cure
(hours) |
Surface Preparation
Methods 3 |
pH Range
5 |
| 12/24 |
72 |
120 |
SSPC-3,11 |
2.5-14 |
An underwater curing version of SAR used for rebuilding
areas underwater or where the component needs to be
put back into underwater service before full cure. Applicable
to both fresh and saltwater service. |
|
Density
(g/ml) |
Coverage
(in 3/kg) |
Mix Ratio by
Weight 1 |
Mix Ratio by
Volume 1 |
Max/Min Build/Coat
(mils) |
| 1.98 |
31 |
2.6:1 |
1.4:1 |
1000/40 |
Number of
Coats |
Working Time
(minutes) |
Minimum Application
Temp (F/C) |
Max Dry Operating
Temp (F/C) |
Dry to Touch
(hours) |
| 1 |
40 |
50/10 |
250/122 |
12 |
Recoat Time
(min/max hours) |
Functional Cure 2
(hours) |
Full Cure
(hours) |
Surface Preparation
Methods 3 |
pH Range
5 |
| 12/24 |
72 |
120 |
SSPC-3,11 |
2.5-14 |
|
|
|
|